Hydrodeoxygenation of benzyl alcohol on transition-metal-containing mixed oxides catalysts derived from layered double hydroxide precursors - Combustion, Energies Propres et Turbulence Accéder directement au contenu
Article Dans Une Revue Catalysis Today Année : 2021

Hydrodeoxygenation of benzyl alcohol on transition-metal-containing mixed oxides catalysts derived from layered double hydroxide precursors

Résumé

M-MgAlO mixed oxide catalysts were prepared by controlled thermal decomposition of layered double hydroxides (LDH) precursors and were tested in the hydrodeoxygenation of benzyl alcohol. LDH with Mg/Al = 3 and 10 at. % M with respect to cations (M = Mn, Fe, Co, Ni, Cu and Zn) were obtained by coprecipitation. A second series of copper-containing catalysts with copper content from 5 to 20 at. % was also prepared. The solids were characterized by X-ray diffraction, N2 adsorption/desorption, temperature-programmed reduction in H2 atmosphere, temperature-programmed desorption of CO2. The influence of the transition metal and, for the copper-containing samples, of the copper loading, reaction temperature, reaction time, amount of catalyst and reduction pre-treatment on the catalytic performance were investigated. With 97% alcohol conversion and 96% selectivity to toluene, Cu15MgAlO is the best hydrodeoxygenation catalyst. It was also tested in the hydrodeoxygenation of 1-heptanol.
Fichier principal
Vignette du fichier
Catalysis Today 2021.pdf (1.47 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03169517 , version 1 (15-03-2021)

Identifiants

Citer

Claudiu Rizescu, Chao Sun, Ionel Popescu, Adriana Urdă, Patrick da Costa, et al.. Hydrodeoxygenation of benzyl alcohol on transition-metal-containing mixed oxides catalysts derived from layered double hydroxide precursors. Catalysis Today, 2021, 366, pp.235-244. ⟨10.1016/j.cattod.2020.04.055⟩. ⟨hal-03169517⟩
75 Consultations
140 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More